What does the code 1100 tell us about aluminum?
What is 1100 Aluminum? 1100 aluminum is also called commercial grade aluminum and is an almost pure aluminum alloy. Generally, 1100 is over 99% aluminum with less than one percent of copper, iron, manganese, silicon, titanium, vanadium, and zinc mixed in for a little extra strength.
Does aluminum have mechanical strength?
Aluminum has typical tensile strength between 40 MPa to 700 MPa. The mechanical strength of aluminum can be increased by cold working and alloying. Copper, magnesium, silicon, manganese and zinc are used as alloying elements. Aluminum doesn’t become brittle at low temperatures and retains its ductility.
What is 1100 Aluminium alloy used for?
Aluminum 1100 can be shaped into many different products, including chemical equipment, railroad tank cars, fin stock, dials, name plates, cooking utensils, rivets, reflectors and sheet metal. The plumbing and lighting industries also use aluminum 1100, as do a wide variety of other industries.
What was the former commercial aluminum designation for 1100 aluminum?
Alternate designations include Al99. 0Cu and A91100. 1100 and its various tempers are covered by the ISO standard 6361 and the ASTM standards B209, B210, B211, B221, B483, B491, and B547.
Is aluminium good under compression?
Among the mechanical properties of aluminum, measuring compressive strength is not obvious because it is a ductile material, besides the fact that pure deformation due to compression is a rarity. Consequently, by convention, the compressive strength of aluminum is considered equal to that of tension.
What is the compression strength of aluminum?
Aluminum – Advantages and Properties of Aluminum
|Property||Minimum Value (S.I.)||Maximum Value (S.I.)|
What percentage of copper does the alloy 1100 contain?
Chemical composition Copper: 0.05–0.20%